Ultra high strength steels are of enormous interest especially in the automotive industry due to their potential in realising
light weight structures and improving the crash behaviour. However the poor formability of these steels limits their application
for many parts in the car body. A solution to this limitation can be a local heat treatment using a laser beam to soften the
material where a high formability is needed. Laser treatment was performed using a Nd:YAG laser with 3 kW maximum power. The
output power was temperature controlled to achieve a constant temperature level during the heat treatment. Large areas are
treated by scanning the surface with the laser beam. The materials under investigation are dual phase (DP), retained austenite
(RA) and martensitic (MS) steels with a tensile strength of 600–1,200 MPa. The microstructure of DP steels consists of martensite
and ferrite. RA steels contain ferrite, martensite and additionally a certain amount of retained austenite which transforms
into martensite during plastic flow. MS steels are fully martensitic which gives them the highest yield strength of all UHS
steels. The various steels were provided as not galvanised sheets (hot or cold rolled) with a thickness of 1.5 mm. Depending
on material and process parameters tempering of martensite, formation of ferrite and transformation of retained austenite
to martensite are observed as a result of the heat treatment. Tensile tests of DP 600, DP 1000 and MS-W 1200 reveal a significant
reduction in yield and tensile strength and an increase in elongation after LHT. The effect is due to tempering of martensite
and in the case of MS-W also due to an increase in volume fraction of ferrite. Tensile tests of RA-K 700 reveal a minor reduction
in yield and tensile strength and a decrease in elongation. This can be attributed to the lower content of retained austenite
which has transformed into martensite during LHT. From this result it can be expected that LHT is not beneficial for high
deformation degrees. Deep drawing of a mock-up geometry using MS-W 1200 and RA-K 700 showed a significant decrease in slide
force (~20%) compared to the initial condition. This results show that laser heat treatment has the potential to improve formability
of UHS steels. |
Year | DOI | Venue |
|---|---|---|
2009 | 10.1007/s11740-009-0186-9 | Production Engineering |
Keywords | Field | DocType |
tensile strength,heat treatment,tensile test,yield strength,initial condition,volume fraction,automotive industry,microstructures,production process | Formability,Tempering,Yield (engineering),Heat treating,Martensite,Austenite,Metallurgy,Ultimate tensile strength,Deep drawing,Engineering | Journal |
Volume | Issue | ISSN |
3 | 4-5 | 1863-7353 |
Citations | PageRank | References |
1 | 0.48 | 0 |
Authors | ||
4 | ||
Name | Order | Citations | PageRank |
|---|---|---|---|
| Reimund Neugebauer | 1 | 6 | 4.80 |
| Sören Scheffler | 2 | 1 | 0.48 |
| Reinhart Poprawe | 3 | 1 | 0.82 |
| Andreas Weisheit | 4 | 1 | 0.82 |